The isi nkịtị uche nkeferrochrome:

Ọkara, obere na obere carbonferrochromeA na-ejikarị silicochrome alloy, chromite na lime mee ka ọ bụrụ ihe akụrụngwa.A na-anụcha ya ma mebie ya site na ọkụ ọkụ eletrik nke 1500 ~ 6000 kV A ma na-arụ ọrụ site na nnukwu ọkụ ọkụ slag (CaO / SiO2 bụ 1.6 ~ 1.8) .Low naMicro carbon ferrochromeA na-emepụtakwa usoro ikpo ọkụ na-ekpo ọkụ n'ọtụtụ buru ibu. A na-eji ọkụ eletrik abụọ na-emepụta ihe, otu maka ịgbaze silicon chrome alloy na nke ọzọ maka agbaze slag nke mejupụtara chrome ore na lime. A na-ekewa mmeghachi omume nnụcha ụzọ abụọ na tankị abụọ. : (1) Mgbe a na-agbanye slag si na ọkụ slag n'ime tank nke mbụ, a na-agbakwunye silicon chromium alloy nke e debere na mbụ n'ime tank ọzọ.N'ihi nnukwu ngafe nke onye na-ahụ maka oxidizing na slag na desiliconization zuru oke, enwere ike nweta micro-carbon ferrochrome nke nwere ihe na-erughị 0.8% silicon na dị ka 0.02% carbon. ② Mgbe slag (nwere ihe dị ka 15% Cr2O3) mmeghachi omume na tank nke mbụ na-akwaga na tank nke abụọ, silicon chromium alloy (nwere 45% silicon) nke a kwadebere na ọkụ ọkụ silicon chromium na-ekpo ọkụ n'ime slag.Mgbe mmeghachi omume gasịrị, a na-enweta silicon chromium alloy (nke nwere ihe dị ka 25% silicon) nke a na-emezigharị na mbụ ma tinye ya na tank nke mbụ maka nkwụsịtụ.Enwere ike ịtụfu slag nwere ihe na-erughị 2 ~ 3% Cr2O3.

A na-eji usoro ikuku oxygen na-anụcha ọkara na obere carbon ferrochrome.A na-eji ikuku carbon ferrochrome mee ihe dị ka akụrụngwa.A na-agbakwunye obere lime na fluorite na ọdọ mmiri a wụrụ awụ iji mee slag n'oge a na-afụ, na silicon chromium alloy ma ọ bụ ferrosilicate na-agbakwunye tupu mmepụta ígwè iji nwetaghachi chromium na slag. Ọfụma nke micro - carbon ferrochrome ga-ekwe omume n'okpuru ụfọdụ oghere. .

Vacuum solid-state decarburization usoro nụchara anụcha, na ezi egweri nke elu carbon ferrochrome dị ka akụrụngwa, ezi egweri nke elu carbon ferrochrome, akụkụ nke oxidizing iri nri dị ka oxidant na mmiri iko ma ọ bụ ndị ọzọ adhesives, bọọlụ mgbali, mgbe obere okpomọkụ ihicha, na Ụdị ọkụ ọkụ ụgbọ ala, ogo agụụ bụ 0.5 ~ 10 mm hg, okpomọkụ nke 1300 ~ 1400 ℃ mbelata okpomọkụ n'okpuru 35 ~ 50 awa, Microcarbon ferrochrome nwere ihe na-erughị 0.03% carbon ma ọ bụ ọbụna ihe na-erughị 0.01% carbon nwere ike nweta.

Ntụle nkwenye nnukwu: mgbe ogbe ahụ na-erughị tọn 10, a ga-ewere ihe na-erughị 10 n'otu n'otu site na akụkụ dị iche iche; akụkụ dị iche iche; Mgbe ogbe ahụ karịrị tọn 30, ọ dịghị ihe na-erughị 30 sample ga-ewereghị usoro site n'akụkụ dị iche iche. Ihe nlele ọ bụla kwesịrị ịdị ka hà nhata, ọkpụkpụ ya abụghị ihe na-erughị 20 * 20mm. Ọnụ ego nlele agaghị adị obere. karịa 0.03% nke nza. A ga-agbaji ihe nlele niile na-erughị 10mm na nkeji nkeji na 1-2kg.Mgbe agwakọtachara, a ga-ekewa ha n'ime akụkụ abụọ hà nhata, otu maka nkwadebe sample na nke ọzọ maka njigide.

N'okpuru ọnọdụ nkịtị, ọ bụ ịlele ọdịnaya nke chromium, na-esote ọdịnaya nke nyocha carbon, ọdịnaya chromium n'okpuru ọnọdụ nkịtị kwesịrị ịdị na 60% ± 0.5.