Silicon manganesealloy (Simn) bụ silicon, manganese, ígwè, obere carbon na ụfọdụ ihe ndị ọzọ. Ọ bụ lumpy ihe na a silvery dara elu.Mmetụta nke mgbakwunye nke silicomanganese na nchara: Ma silicon na manganese nwere mmetụta dị mkpa na njirimara nke ígwè, dabere na ego agbakwunyere na mmetụta jikọtara ya na ihe ndị ọzọ alloying. Dị ka contenr nke silicon na manganese, ọ nwere ike kewaa. n'ime FeMn68Si18, FeMn64Si16 na ngwaahịa ahaziri ahazi na-abụghị ọkọlọtọ.

Silicon manganese alloyisi akụrụngwa bụ manganese ore, manganese-ọgaranya slag, silica, coke, wayo, ect.Si-mn alloy nwere ike gbazee site na-aga n'ihu na-arụ ọrụ na nnukwu, ọkara na obere ore ọkụ.

Ọ bụ ngwakọta nke manganese na silicon dị ọnụ ala ma bụrụkwa ngwaahịa a na-ahọrọ maka ndị na-emepụta ígwè.A na-eri ya na ngwaahịa nchara niile ma jiri ya mee ihe dị elu na 200 usoro igwe anaghị agba nchara, alloy steel na manganese ígwè.

Ngwa:

①Silicon manganese alloy bụ isi ọrụ maka ígwè-eme bụ alloying gị n'ụlọnga, compound deoxidizer, desulfurizer.

② Ọ nwere ike na-egosipụta nkedo nkedo arụ ọrụ anụ ahụ na n'ibu ikike, ike ike na eyi-eguzogide ihe onwunwe.

③Ọ bụ onye na-ebelata ohere maka imepụta ọkara na obere carbon ferromanganese na imepụta manganese ígwè site na usoro ọkụ silicon ọkụ eletrik.

Akara International nke Silicon Manganese Alloy (GB4008-2008)

Aha ika

Ngwakọta kemịkalụ (%)

Mn

Si

C

P

S

FeMn64Si27

60.0-67.0

25.0-28.0

0.5

0.10

0.15

0.25

0.04

FeMn67Si23

63.0-70.0

22.0-25.0

0.7

0.10

0.15

0.25

0.04

FeMn68Si22

65.0-72.0

20.0-23.0

1.2

0.10

0.15

0.25

0.04

FeMn62Si23
(FeMn64Si23)

60.0-65.0

20.0-25.0

1.2

0.10

0.15

0.25

0.04

FeMn68Si18

65.0-72.0

17.0-20.0

1.8

0.10

0.15

0.25

0.04

FeMn62Si18
(FeMn64Si18)

60.0-65.0

17.0-20.0

1.8

0.10

0.15

0.25

0.04

FeMn68Si16

65.0-72.0

14.0-17.0

2.5

0.10

0.15

0.25

0.04

FeMn62Si17
(FeMn64Si16)

60.0-65.0

14.0-20.0

2.5

0.20

0.25

0.30

0.05


Oge nzipu: Mee-14-2021